Mining & Coal Preparation 

Coal-Fired Power Plants  

Pulp & Paper

Cement Processing

Steel Processing

Wear & Abrasion Solutions

2

Table of Contents

About ITW Wear & Abrasion Group 

4 

 

Product Technologies 

5 

 

Wearing Compounds 

6

Belting & Rubber Repair 

10

Urethane Casting Compounds 

12

Corrosion Repair Compounds 

14

Metal Repair Epoxies 

16

Crusher Backing Compounds 

20

Surface Preparation 

22

Agency Approvals 

24

Product Index 

25

3

About ITW Wear & Abrasion Group 

4

ITW Wear & Abrasion Group is a global Sales, Marketing, and Technical Support group that markets, supports and promotes  

well-recognized brands such as Densit®, Devcon® and Korrobond.

We are utilizing ITW’s global network of R&D facilities, technology centers, and manufacturing facilities within the ITW Polymers 

Division to develop and provide one of the most extensive lines of wear and abrasion products available. Our target industries 

include, but are not limited to: Mining, Coal Preparation, Cement Plants, Coal-Fired Power Plants, Pulp & Paper and Chemical 

Processing.

In industrial plants, unexpected or unscheduled plant shutdowns caused by wear in processing machinery, are costly and thus 

reduce competitiveness. Wear and abrasion or corrosion is especially familiar in those industries that process or use large 

quantities of abrasive material in their production process. ITW Wear & Abrasion Group’s experienced sales team has detailed 

knowledge and experience to solve your problem. ITW Wear & Abrasion Group has the solution; whether you need to rebuild 

equipment to original specs or prevent failures from occurring in a preventative maintenance program.

About ITW, Our Parent Company

Illinois Tool Works Inc. (NYSE: ITW), a Fortune 200 company, is a diversified manufacturing company that delivers specialized ex-

pertise, innovative thinking and value-added products to meet critical customer needs in a variety of industries.  ITW businesses 

serve local customers and markets around the globe, with a significant presence in developed as well as emerging markets. With 

$17.8 billion in 2011 revenues, ITW employs approximately 60,000 women and men in 58 countries who adhere to the highest 

ethical standards. These talented individuals, many of whom have specialized engineering or scientific expertise, contribute to 

our global leadership in innovation. We are proud of our broad portfolio of nearly 12,000 active patents. For more information 

about ITW, please visit www.ITW.com.

Danvers, U.S.A

São Paulo

Moscow

Rushden, U.K

Medak District A.P. 

Osaka  

Shanghai

Sydney

5

Belting and Rubber Repair Compounds

 are flexible urethane   

structural technologies for repairing worn or damaged SBR conveyor 

belts, rubber lined equipment such as pipes and tanks in mines, 

quarries, and coal-fired power plants.  These products are in a non-

sag putty for patching and repairing linings along with self-leveling 

thixotropic versions that create a smooth surface for repairing  

conveyor belts.

Metal Repair Epoxies 

are metal-filled epoxy technology that allows 

for fast, economical, permanent repairs to power plant and mining 

equipment.  The epoxies cure quickly; can be machined, tapped and 

corrosion resistant to harsh chemicals.  These products are  

available in liquid formulas that can be used for mold patterns, 

holding fixtures and forming dies. 

Wearing Compounds 

are specially formulated wear-resistant 

epoxy coatings that protect dry materials handling and storage 

equipment from sliding abrasion, impact and wear. These products 

are trowelable, non-sag putties available in large particulate, high 

impact, and high temperature formulas.   

Tile Adhesives are high strength, room temperature curing, 

trowelable adhesives that bond ceramic tiles to metal.

Corrosion Repair Compounds

 are ceramic filled epoxy technology to 

make permanent repairs to pumps, shafts, pipes, and tanks where a  

corrosion-resistant polymer is needed to protect all metals against 

corrosion and erosion in slurry applications.  These products apply 

easily with a brush or in a creamy putty consistency that allows you to 

be back in service within 3-5 hours.

Product Technologies

Devcon

®

 DFense Blok

™

 

A bead-filled epoxy compound formulated 

to significantly outlast traditional wear and 

abrasion products while providing superior 

protection.

• 4X better abrasion resistance than  

    competition 

• 7X better drop impact strength than  

    ceramic tile

Item # 

  Size

11330          30lb 

Devcon

®

 DFense Blok

™

  Fast 

Cure (FC)

A bead-filled epoxy compound that allows 

equipment to be returned to service in 2 

hours.  

• Non-sagging , good adhesion

• Withstands operating temperature, as  

    high as 300°F

Item # 

 Size

11350        9lb 

Devcon

®

 DFense Blok

™

 Surface 

Wetting Agent

A thixotropic epoxy gel system that 

improves the ease of application and 

cured adhesion properties of DFense 

Blok™ 

• Zero wait time before applying DFense  

   Blok™

• Orange color for easy visual inspection

 

Item # 

 Size

11340   1lb

Devcon

®

 DFense Blok

™

 Quick 

Patch

 

The only ceramic bead-filled wear and 

abrasion resistant epoxy for emergency 

repair. 

• Eliminates down-time with exceptionally  

    fast cure

• Repairs holes, leaks and cracks

 

Item # 

  Size

11320    1lb

Specially formulated wear-resistant epoxy coatings that protect dry materials handling and storage equipment from 

abrasion, corrosion and wear. The DFense Blok™ product line is truly an advanced epoxy technology with quicker 

functional cure times and better abrasion resistance.

Wearing Compounds

Devcon

® 

DFense Blok

™

 Power 

Mixer

Recommended for most effective way to 

thoroughly mix DFense Blok™ Wearing 

Compound. 

• Durable steel paddle with three blades;  

    2X faster than drill-style mixers  

• Plugs into standard 120V outlet.   

Item # 

Size

11301   81lb

Watch our

   

Impact Test!

6

7

Physical 

Properties

Devcon

®

  

DFense Blok™

Devcon

®

  

DFense Blok™  

Surface Wetting Agent

Devcon

®

  

DFense Blok™  

Fast Cure (FC)

Devcon

®

  

DFense Blok™  

Quick Patch

Color 

Grey 

Orange

Grey

Grey

Mix ratio by weight / volume 

resin:hardener

2:1 / 100:45

2:1/100:44

2:1/2:1

1:1/1:1

Mixed viscosity   cP

Putty

Thixotropic Gel

Putty

Putty

Functional cure  hours

4-5

4-5

2-3

30 minutes

Pot life  minutes @ 75˚F

25

12-15

15

4 

Specific volume inches

3

 /pound

12.6

24.7

13.8

14.89

Coverage per pound 

inches

2

  @ 1⁄4" thickness

47

1860 @ 12mils

53

60

Cured hardness

 (ASTM D2240)   Shore D 

77

71

80

84

Cured shrinkage

 (ASTM D2566) inch/inch 

0.0005

N/A

0.0008

0.0010

Adhesive tensile shear 

(ASTM D1002)    psi 

2,616

2,616

2,764

2,495

Compressive strength

 (ASTM D695)    psi

7,145

5,032

7,178

6,166

Flexural strength 

(ASTM D790)    psi  

7,876

6,700

7,488

4,880

Coefficient of thermal expansion  

(ASTM D696)[(in)/(in x ˚F)] x 10

-6

29

N/A

33

31

Dielectric constant (ASTM D150)    1 kHz

49.0

N/A

45

51

Maximum continuous dry  

service temperature   ˚F

300

300

300

200

Technical Information

Chemical Resistance

Devcon

®

  

DFense Blok™

Devcon

®

  

DFense Blok™ Surface  

Wetting Agent

Devcon

®

  

DFense Blok™  

Fast Cure (FC)

Devcon

®

  

DFense Blok™  

Quick Patch

ACIDS
Acetic 10%
Hydrochloric 10%
Sulfuric 10%
ALCOHOLS
Methanol
Isopropanol

KETONES 
Acetone
Methyl ethyl ketone

ALKALIS 

Ammonium hydroxide 20%

Sodium hydroxide 10%

 HYDROCARBONS 
Gasoline (unleaded)
Mineral spirits

CHLORINATED  

HYDROCARBONS
1-1-1 Trichloroethane

SALTS 
Sodium chloride
Trisodium phosphate

Key:               Excellent               Very Good              Fair               Poor

NOTES:

 

 

1

  

Coverage in inches

2

 / 20.4 pound unit , 

2

  

Three-part system, beads separate

Devcon

®

 Wear Guard

™

 Fine Load

 

High-density, micro-alumina ceramic  

bead-filled epoxy system for  

protecting equipment that handles  

particulate smaller than 1⁄ 8".

• Withstands operating temperatures  

    as high as 300°F 

• Outstanding resistance to a wide  

   range of chemicals

Item # 

Size

11470  30lb 

Devcon

®

 Wear Guard

™

 High Temp

High-density, ceramic bead-filled 

epoxy system for maximum wear and 

abrasion resistance in high temperature 

applications.

• Heat-cured, trowelable system that  

   gives up to 30% improvement over  

   conventional wear compounds 

• Withstands continuous service  

   temperatures to 450°F 

 

Item # 

Size

11480  30lb

Devcon

®

 Tile Adhesive

High-strength, trowelable adhesive that 

cures at room temperature.

• Bonds ceramic tile to vertical, curved,  

    and overhead surfaces and repairs  

    loose ceramic tiles 

• Excellent chemical resistance to acids  

    and alkalis

Item # 

Size

11495  20lb

Specially formulated wear-resistant epoxy coatings that protect dry materials handling and storage equipment 

from abrasion, corrosion and wear. These products are trowelable, non-sag putties available in large particulate, 

high impact, and high temperature formulas.

Devcon

®

 Wear Guard

™

 High Load 

Alumina ceramic bead-filled epoxy system 

with outstanding abrasion resistance for 

severe service conditions with particulate 

greater than 1⁄8".

• Trowels onto overhead or vertical  

    surfaces without sagging 

• Ideal for repairing scrubbers, ash  

    handling systems, pipe elbows,  

    screens, and chutes 

Item # 

Size

11490  30lb 

Devcon

®

 Wear Guard

™

 High Impact

 

High density micro alumina ceramic  

bead-filled epoxy system with a flexible 

additive for superior impact and abrasion 

resistance 

• Non sagging putty in a creamy 

 

    consistency 

• High compression and impact strength 

Item # 

Size

11460  30lb 

Devcon

®

 Combo Wear FC

High-tech, three-component (2 bead 

sizes plus silicon carbide) compound for 

repairing process equipment quickly and 

returning it to service in as little as 1-1/2 

hours. 

• Excellent adhesion to metal, ceramic,  

    and concrete surfaces 

• Ideal for cracks in large coal fuel lines 

Item # 

Size

11450  9lb 

Devcon

®

 Wear Guard

™

 Ultra

Alumina ceramic bead-filled epoxy system 

with outstanding abrasion resistance for 

severe service conditions. 

• Outstanding Wear Resistance 

• Extends Equipment Operating Cycles

 

Item # 

Size

11475  30lb

Devcon

® 

 Carbide Putty

Silicone carbide-filled epoxy putty for 

economical protection against sliding wear 

and abrasion.  

• Excellent abrasion resistance in 

 

    aggressive industrial  environments 

• Handles particulates less than 1/16”

Item # 

Size

10050   3lb

10080 20lb

8

Wearing Compounds

Devcon

®  

HV Tile Adhesive 

High-strength, trowelable adhesive  

compound for bonding tile, with a 35 

minute working time.

• High viscosity, great non-sag adhesive

• Fills gaps and joints in crushers prior to  

    backing compounds

Item # 

Size

11489      20llb

Technical Information

Key:               Excellent               Very Good              Fair               Poor

Chemical 

Resistance

Devcon

®

 

Wear Guard™ 

Fine Load

Devcon

®

 

Wear Guard™ 

High Load

Devcon

® 

Wear Guard™ 

High Temp

Devcon

®

 

Wear Guard

™

 

High Impact

Devcon

®

 

Wear Guard

™

 

Ultra

Devcon

®

 

Combo Wear FC 

(Fast Cure)

Devcon

®

 

Tile Adhesive 

Devcon

®

 

HV Tile Adhesive

Devcon

®

  

Carbide Putty

ACIDS
Acetic 10%
Hydrochloric 10%
Sulfuric 10%

ALCOHOLS
Methanol
Isopropanol

KETONES 
Acetone
Methyl ethyl ketone

ALKALIS 

Ammonium hydroxide 20%

Sodium hydroxide 10%

 HYDROCARBONS 
Gasoline (unleaded)
Mineral spirits

CHLORINATED  

HYDROCARBONS
1-1-1 Trichloroethane

SALTS 
Sodium chloride
Trisodium phosphate

9

NOTES:

 

  

2

  

Three-part system, beads separate

Physical 

Properties

Devcon

®

  

Wear Guard™  

Fine Load

Devcon

®

  

Wear Guard™ 

High Load

Devcon

®

  

Wear Guard™

 High Temp

Devcon

®

 

Wear Guard

™

 

High Impact

Devcon

®

 

Wear Guard

™

 

Ultra

Devcon

®

 

Combo Wear FC 

(Fast Cure)

Devcon

®

  

Tile Adhesive

Devcon

®

  

HV Tile 

Adhesive

Devcon

®

  

Carbide Putty

Color 

Grey

Grey 

Grey 

Dark Grey 

Grey

Grey 

White

Grey

Grey

Mix ratio by weight /volume 

resin:hardener

2:1 / 2:1

2:1 / 2:1

13.7:1 / 6:1

2.5:1 / 2.5:1

2.15:1:5.65

2

2:1 / 2:1

 1.1:1 / 1:1

 1.1:1 / 1:1

8:1 / 4:1

Mixed viscosity   cP

Putty

Putty

Putty

Putty

Putty

Putty

Putty

Putty

Putty

Functional cure hours

6-8

6-8

Heat Cured

6-8

16

2-3

12

12

16

Pot life minutes @ 75˚F

30

30

120

30

20

7

240

35

50

Specific volume inches

1

/pound

12.4

12.9

14.3

12.4

11.4

12.4

19.2

19

15.9

Coverage per pound 

inches

2

  @ 1⁄4" thickness

50

50

60

50

46

50

76.8

76

64

Cured hardness 

 (ASTM D2240)   Shore D 

87

87

87

85

87

87

81

81

85

Cured shrinkage  

(ASTM D2566) inch/inch 

0.0006

0.0006

0.0010

0.0006

0.0004

0.0008

0.0010

0.0010

0.0009

Adhesive tensile shear  

(ASTM D1002)    psi 

1,375

1,474

2,300

2,567

1,425

1,450

2,890

1,825

1,350

Compressive strength  

(ASTM D695)    psi

11,000

11,000

13,200

7,250

13,910

11,000

9,620

11,800

8,160

Flexural strength  

(ASTM D790)    psi  

7,190

7,140

8,220

6,144

7,220

7,140

5,480

5,400

5,480

Coefficient of thermal  

expansion (ASTM D696)[(in)/(in 

x ˚F)] x 10

-6

34

32

27

34

26

34

14

14

14

Dielectric constant  

(ASTM D150)    1 kHz

46.0

41.0

38.0

46.0

40.0

41.0

46.0

45.0

25.0

Maximum continuous dry 

service temperature   ˚F

300

300

450

300

300

300

200

200

250

10

Devcon

®

 Flexane

®

 80 Putty

Trowelable urethane for repairing and 

lining process equipment exposed to wear, 

abrasion, vibration or  

expansion/contraction.

• Service temperatures to 180°F in dry 

    environments and  120°F in wet  

    environments 

• Bonds to metal, concrete, rubber,  

 

    wood, and fiberglass surfaces 

Item # 

Size

15820 1lb

15850  4lb

Devcon

® 

Flexane

®

 High  

Performance Putty 

Trowelable lining for maximum protection 

against abrasion, gouging and impact.

• Cures to a tough (tear strength 400  

    pli), resilient rubber compound 

    (Hardness 78 Shore A)

• Bonds to metal, rubber, wood, 

 

    fiberglass, and concrete 

Item # 

Size

15330 1lb

Flexible urethane technologies for repairing worn or damaged SBR conveyor belts, rubber lined equipment such as pipes 

and tanks in mines, quarries, and coal-fired power plants.  These products are in a non-sag putty for patching and  

repairing linings along with self-leveling thixitropic versions that create a smooth surface for repairing conveyor belts.

Devcon

®

 Flexane

®

 Belt Repair Kit

Flexane

®

 80 Putty belt repair kit for 

repairing holes and tears in conveyor belts. 

• Makes belt repairs covering up to 188    

    square inches at ¼” thickness

• Repairs and bonds to metals, concrete,  

    rubber, wood, and  fiberglass

Item # 

Size

15165 Kit

Belting & Rubber Repair

Devcon

® 

400ml Dispensing 

System

Manual dispensing gun and custom design 

mixing nozzle for 4:1 400 ml systems.

• Used with Flexane

®

 Fast Cure Putty  

   #15049  &  Flexane

®

 Fast Cure Liquid  

   #15050

Item # 

     Size     

15043  400ml gun

15047 

Nozzle (Ø.394” 4:1 ratio)

 

Devcon

® 

Flexane

®

 Fast Cure 

Putty 

Black Flexane

®

 Fast Cure thickens to a 

putty in seconds providing superior  

flexibility, elongation and adhesion to  

rubber. 

• Light service duty in 3 hours 

• Thixotropic , creamy formula which  

 

    thickens in time 

• Dispenser #15043

 (manual)  

    Nozzle #15047

Item # 

     Size               

15049 

     400ml cartridge   

  

Devcon

® 

Flexane

®

 FC Liquid 

A convenient, time-saving method of  

filling expansion joints and repairing 

rubber.

•8-minute working time 

•No-mess dispensing with fast, easy,  

 

  400ml reusable cartridges 

• Dispenser: #15043

 (manual)  

   Nozzle #15047

Item # 

     Size               

15050 

      400ml cartridge   

Devcon

® 

Flexane

®

 Brushable 

High-performance brushable urethane for 

protection against abrasion and impact. 

• Excellent for repairing/coating 

 

   rubber-lined pumps, tanks  and valves

• Applies in thicknesses of 50 mils in  

 

    one application 

 

Item # 

Size

15350 1lb

Devcon

®

 R-Flex™

NEW! The newest belt repair product in the 

market place. A self-leveling urethane kit 

for repairing holes and tears in conveyor 

belts. Also used to cover and protect clips /

pins from scrapers.

• Functional cure in 90 minutes

• High adhesion with surface pull of the    

    SBR rubber

• Kit includes surface conditioner

Item # 

Size

15550  4lb

11

Technical Information

Physical Properties

Devcon

®

 R-Flex

™

Devcon

®

 Flexane

® 

Belt Repair Kit

Devcon

®

 Flexane

®

  

 80 Putty

Devcon

®

 Flexane

®

  

Brushable

Devcon

®

 Flexane

®

  

High Performance 

Putty

Devcon

®

 Flexane

®

  

Fast Cure Putty

Devcon

®

 Flexane

®

  

 Fast Cure Liquid

Color 

Black

Black

Black

Black

Black

Black

Grey 

Mix ratio by weight   

resin:hardener

88:12

72:28

72:28

80:20

94:6

80:20

80:20

Mixed viscosity   cP

Putty

Putty

Putty

40,000

Putty

Putty

5,800

Pot life minutes @ 75˚F

4

20

20

45

10

8

8

Specific volume inches

3

/

pound

27.4

23.5

23.5

26.0

23.5

23.5

26.5

Coverage per pound inches

2

   

@ 1/4" thickness

110

94

94

104

94

94

106

Functional cure hours

1 1/2

12

12

18

16

3

2

Demolding time hours

N/A

N / A

N/A

N/A

N/A

N/A

N/A

Cured hardness

(ASTM D2240)    Shore A

92

87

87 

86

78

88

94

Cured shrinkage

(ASTM D2566)    inch/inch

NA

0.0014

0.0014

0.232

0.12

2

0.0014

0.0018

Tensile strength

(ASTM D412)    psi

1,462

1,700

1,700

3,500

4,500

2,400

3,300

Tear resistance

(ASTM D624)    pli

270

300

300

400

400

275

430

Abrasion resistance   

weight loss

1

270

280

280

90

140

220

330

Maximum elongation

(ASTM D412)    %

421

300

300

600

600

500

450

Dielectric strength

(ASTM D149 )    volts/mil

350

350

350

340

350

350

350

Maximum continuous wet 

service temperature   ˚F

120

120

120

120

120

120

120

Maximum continuous dry

service temperature   ˚F

180

180

180

180

180

180

180

Key:               Excellent               Very Good              Fair               Poor

NOTES:

 

 

1

  

Taber H-18 wheel (mg/ 1,000 revolutions @ 1,000 gram load)  

2

  

Due to solvent loss

Chemical Resistance

Devcon

®

 R-Flex™

Devcon

®

 Flexane

® 

Belt Repair Kit

Devcon

®

 Flexane

®

  

 80 Putty

Devcon

®

 Flexane

®

  

Brushable

Devcon

®

 Flexane

®

  

High Performance 

Putty

Devcon

®

 Flexane

®

  

Fast Cure Putty

Devcon

®

 Flexane

®

  

 Fast Cure Liquid

ACIDS 
Acetic 10%
Hydrochloric 10%
Sulfuric 10%
Sulfuric 50%
Phosphoric 10%

ALCOHOLS 
Methanol
Isopropanol

 

KETONES 
Acetone
Methyl ethyl ketone

ALKALIS 
Ammonium hydroxide 20%
Sodium hydroxide 10%

HYDROCARBONS 
Gasoline (unleaded)
Mineral spirits

SALTS 
Sodium chloride
Trisodium phosphate
Aluminum sulfate 10%
Sodium carbonate 10%

Belting & Rubber Repair

Flexible urethane technologies for repairing worn or damaged SBR conveyor belts, rubber lined equipment such as pipes 

and tanks in mines, quarries, and coal-fired power plants.  These products are in a non-sag putty for patching and  

repairing linings along with self-leveling thixotropic versions that create a smooth surface for repairing conveyor belts.

Devcon

®

 Flexane

®

 80 Liquid

Medium-viscosity (10,000 cP) urethane 

fills voids completely and faithfully  

reproduces mold detail.  

• Cures to semi-rigid rubber 

 

   (Shore A 87)

• Cures at room temperature to a  

   semi-rigid rubber material 

Item # 

Size

15800 1lb

15810 10lb 

Devcon

®

 Flexane

®

 94 Liquid

Low-viscosity (6,000 cP) urethane fills 

voids completely and faithfully reproduces 

mold detail. 

• Similar to Flexane

®

 80 Liquid, but  

   cures to (Shore A 97)

• Requires only a five hour demolding  

    time

Item # 

Size

15250 1lb

15260 10lb 

Devcon

®

 Flex-Add

™

 

Used with Flexane

®

 80 Liquid to produce 

a more flexible urethane.

• Creates a lower durometer 

 

   castable urethane 

• Can match existing hardness of  

   rubber 

Item # 

Size

15940  8oz 

Devcon

® 

Liquid Release Agent

Silicone release agent prevents Devcon’s 

epoxy and urethane compounds from  

sticking to patterns or mold surfaces.

• Produces a high gloss finish 

• Facilitates the accurate duplication    

    of intricate details

Item # 

Size

19600 1pt

 

Devcon

® 

Flexane

®

 Primer

Required for maximum adhesion of  

Flexane

®

 products.

FL-10 Primer for all metals.

FL-20 Primer for rubber, wood, fiberglass 

and concrete.

FL-40 Primer for rubber. Ensures ultimate 

peel strength (greater than 80 psi)

Item # 

Primer 

Size

15980  FL-10 

4oz

15985  FL-20 

4oz

15984  FL-40 

4oz

12

13

Physical Properties

Devcon

®

 Flexane

®

  

80 Liquid

Devcon

®

 Flexane

®

  

94 Liquid

Color 

Black

Black

Mix ratio by weight  resin:hardener

77:23

69:31

Mixed viscosity   cP

10,000

6,000

Pot life minutes @ 75˚F

30

10

Specific volume inches

3

/pound

26.5

26.5

Coverage per pound inches

2

  @ 1/4" thickness

106

106

Functional cure hours

16 

16 

Demolding time hours

10

5

Cured hardness (ASTM D2240)    Shore A

87 

97

Cured shrinkage (ASTM D2566)    inch/inch

0.0018

0.0014 

Tensile strength (ASTM D412)    psi

2,100

2,800

Tear resistance (ASTM D624)    pli

350

415

Abrasion resistance weight loss

1

285

330

Maximum elongation (ASTM D412)    %

650

500

Dielectric strength (ASTM D149 )    volts/mil

350

350

Maximum continuous wet service temperature   ˚F

120

120

Maximum continuous dry service temperature   ˚F

180

180

Technical Information

Key:               Excellent               Very Good              Fair               Poor

Chemical Resistance

Devcon

®

 Flexane

®

  

 80 Liquid

Devcon

®

 Flexane

®

  

 94 Liquid

ACIDS 
Acetic 10%
Hydrochloric 10%
Sulfuric 10%
Sulfuric 50%
Phosphoric 10%

  

 

 

 

ALCOHOLS 
Methanol
Isopropanol

  

 

 

 

KETONES 
Acetone
Methyl ethyl ketone

  

 

 

 

ALKALIS 
Ammonium hydroxide 20%
Sodium hydroxide 10%

  

 

 

 

HYDROCARBONS 
Gasoline (unleaded)
Mineral spirits

 

 

 

SALTS 
Sodium chloride
Trisodium phosphate
Aluminum sulfate 10%
Sodium carbonate 10%

  

 

 

 

NOTES:

 

 

1

  

Taber H-18 wheel (mg/ 1,000 revolutions @ 1,000 gram load)  

Devcon

® 

Titanium Putty

High-performance, nonrusting 

titanium-reinforced epoxy putty for making 

repairs that can be precision machined.  

• Withstands heavy loads in harsh  

    chemical environments 

• High compressive strength

Item # 

Size

10760   1lb

10770   2lb

Devcon

® 

Ceramic Repair Putty

Trowelable,  alumina-filled epoxy  

compound for rebuilding, smoothing and 

protecting processing equipment exposed 

to corrosion, erosion, cavitation, chemicals 

and acids. 

• Temperature range up to 350°F 

• Excellent for filling voids and 

 

   rebuilding metal castings 

Item # 

Size

11700   3lb

Devcon

® 

Ceramic Repair 

Compound

Trowelable, alumina-filled epoxy  

compound with a 45-minute pot life and 

larger kit size for bigger jobs of 

 

rebuilding, smoothing and protecting 

processing equipment. 

• Temperature range up to 350°F 

• Excellent for filling voids and 

 

    rebuilding metal castings 

Item # 

Size

11730 32lb

Devcon

® 

Brushable Ceramic

When applied in a 15-20 mil coating, this 

low-viscosity, alumina-filled, brushable 

epoxy compound produces a smooth, 

protective barrier against wear, abrasion, 

corrosion, erosion and chemical attack. 

• Temperature range up to 350°F 

• Brushable Ceramic white is NSF 61  

    Certified. 

 

Item # 

Size

11760 

2lb (red)

11762 

12lb (red)

11765 2lb (blue)
11767 12lb (blue)
11770 

2lb (white) 

Ceramic filled epoxy technology used to make permanent repairs to pumps, shafts, pipes, and tanks where a  

corrosion-resistant polymer is needed to protect all metals against corrosion and erosion in slurry applications.   

These products apply easily with a brush or trowel.

Corrosion Repair Compounds

14

15

Technical Information

Physical Properties

Devcon

® 

Titanium 

Putty

Devcon

® 

Brushable Ceramic

Red, Blue

Devcon

® 

Brushable Ceramic

White

Devcon

®  

Ceramic Repair 

Putty

Devcon

®  

Ceramic Repair 

Compound

Color 

Grey

Red, Blue 

White

Dark Blue

Dark Blue

Mix ratio by weight / volume   

resin:hardener

4.3:1 / 3:1

5.6:1 / 3.4:1

8:5:1 / 5:6:1

7:1 / 4.3:1

4.7:1 / 3.3/1

Mixed viscosity   cP

Putty

32,000

40,000

Putty

Putty

Functional cure hours

16

16

16

16

16

Pot life minutes @ 75˚F

21

40

21

25

45

Specific volume inches

3

/pound

11.7

17.5

16.5

16.4

17.9

Coverage per pound inches

2

 @ 1⁄4" thickness

47

7.6

1

7.6

1

66

72

Cured hardness  

(ASTM D2240)    Shore D 

87

90

87

90

86

Cured shrinkage  

(ASTM D2566)    inch/inch 

0.0010

0.0020

0.0020

0.0022

0.0024

Adhesive tensile shear  

(ASTM D1002)    psi 

2,000

2,000

2,000

2,000

2,231

Compressive strength  

(ASTM D695)    psi

15,200

15,200

15,200

12,700

10,240

Flexural strength  

(ASTM D790)    psi  

7,700

3,800

3,800

6,475

5,870

Modulus of elasticity  

(ASTM D638)    psi x 105      

9.5

8,000

8,000

9.0

8.1

Coefficient of thermal expansion (ASTM D696) 

[(in)/(in x ˚F)] x 10

-6

22

9.0

9.0

17

20

Thermal conductivity (ASTM C177) 

[(cal x cm)/(sec x  cm2 x ˚C)]  x 10

-3

1.95

19

19

1.88

1.72

Dielectric constant  

(ASTM D150 )    1 kHz

44.8

1.92

1.92

41.0

38.0

Dielectric strength  

(ASTM D149 )    volts/mil 

56

382

382

370

350

Maximum continuous dry 

service temperature   ˚F

350

350

350

350

350

Chemical Resistance

Devcon

® 

Titanium 

Putty

Devcon

® 

Brushable Ceramic

Red, Blue

Devcon

® 

Brushable Ceramic

White

Devcon

®

  

Ceramic Repair 

Putty

Devcon

®

  

Ceramic Repair 

Compound

ACIDS 
Acetic 10%
Hydrochloric 10%
Sulfuric 10%

ALCOHOLS 
Methanol
Isopropanol

KETONES 
Acetone
Methyl ethyl ketone

ALKALIS 
Ammonium hydroxide 20%
Sodium hydroxide 10%

HYDROCARBONS 
Gasoline (unleaded)
Mineral spirits

CHLORINATED HYDROCARBONS
1-1-1 Trichloroethane

SALTS 
Sodium chloride
Trisodium phosphate

Key:               Excellent               Very Good              Fair               Poor

NOTES:

 

 

1

  

Coverage (feet

2

 @ 15mils)

Metal Repair Epoxies

16

Devcon

® 

Plastic Steel

®

 Liquid (B)

A pourable steel-filled epoxy that provides 

accurate detail reproduction in making 

holding fixtures, light gauge forming dies 

and molds. 

• Can be drilled, tapped and machined

• Qualifies under Federal Specification  

    MMM-A-1754, Adhesive/Sealing

 

Item # 

Size

10210 1lb

10220  4lb

10230 25lb 

Devcon

® 

Aluminum Liquid (F-2)

Aluminum-filled pourable epoxy for making 

molds, patterns and holding fixtures.  

• It can be drilled, tapped and machined

• Hardens in just over 1 hour; cures in 16  

    hours 

• Qualifies under Federal Specification  

    MMM-A-1754, Adhesive/Sealing

Item # 

Size

10710 1lb

10720 3lb

Devcon

®

 Plastic Steel

®

 Putty (A)

The original metal-filled epoxy putty, it is 

ideal for repairing areas where welding or 

brazing would be impractical. 

• Can be drilled, tapped and machined. 

• Conforms to the requirements of   

 

    MIL-PRF-24176C, Type I 

Item # 

Size

10110 1lb

10120  4lb

10130 25lb

Devcon

® 

Plastic Steel

®

 5 Minute

®

 

Putty (SF)

Fast-curing, steel-filled epoxy for  

emergency repairs at temperatures as low 

as 40°F. 

• Repaired parts can be returned to 

 

    service within one hour

• Mixes, applies, and cures at 

    tempera tures as low as 40°F

Item # 

Size

10240   1lb

Devcon

®  

Stainless Steel Putty 

(ST)

Stainless steel-filled epoxy putty for  

patching, repairing and rebuilding stainless 

steel surfaces as well as food processing 

equipment. 

• Bonds to ferrous and non-ferrous metals

• NSF 61 Certified

Item # 

Size

10270   1lb

Devcon

® 

 Aluminum Putty

Aluminum-filled epoxy putty for 

dependable nonrusting repairs to 

aluminum castings, machinery and 

equipment. 

• Can be machined drilled or tapped using 

 

    conventional metalworking tools 

• Widely used in HVAC applications, it  

    conforms to requirements of  

    MIL-PRF-24176C, Type II

Item # 

Size

10610 1lb

10620 3lb

Metal-filled epoxy technology that allow for fast economical permanent repairs to power plant and mining equipment. 

They can be machined, tapped and drilled, and corrosion resistant to harsh chemicals.  These products are available in 

pourable versions that can be used to provide accurate detail reproductions for short run prototype mold patterns,  

holding fixtures and forming dies.

17

Technical Information

Physical Properties

Devcon

® 

Plastic Steel

®

 

Putty 

(A)

Devcon

® 

Plastic Steel

® 

Liquid (B)

Devcon

® 

Plastic Steel

®

 

5 Minute

®

 Putty 

(SF)

Devcon

® 

Stainless Steel 

Putty 

(ST)

Devcon

® 

Aluminum 

Putty 

(F)

Devcon

® 

Aluminum 

Liquid (F-2)

Color 

Dark Grey

Dark Grey

Dark Grey

Grey

Aluminum

Aluminum 

Mix ratio by weight / volume   

resin:hardener

9:1 / 2.5:1

9:1 / 3:1

1.7:1 / 1:1

11:1 / 3.75:1

9:1 / 4:1

9:1 / 5:1

Mixed viscosity   cP

Putty

15 / 25,000 

Putty

Putty

Putty

15 / 25,000

Functional cure hours

16

16

1

16

16

16

Pot life minutes @ 75˚F

45

45

5

58

60

75

Specific volume inches

3

/pound

11.9

13.1

12.2

12.4

17.5

17.5

Coverage per pound inches

2 

@ 1⁄4" 

thickness

48

52

49

50

70

70

Cured hardness  

(ASTM D2240)    Shore D 

85

85

85

85

85

85

Cured shrinkage  

(ASTM D2566)    inch/inch 

0.0006

0.0006

0.0006

0.0010

0.0008

0.0009

Adhesive tensile shear  

(ASTM D1002)    psi 

2,800

2,800

2,026

2,385

2,600

2,700

Compressive strength  

(ASTM D695)    psi

8,260

10,200

10,400

8,400

8,420

9,820

Flexural strength  

(ASTM D790)    psi  

5,600

7,480

7,680

5,280

6,760

7,180

Modulus of elasticity  

(ASTM D638)    psi x 10

5

      

8.5

8.5

7.5

8.0

8.0

7.5

Coefficient of thermal  

expansion (ASTM D696) 

[(in)/(in x ˚F)] x 10

-6

48

38

34

34

29

50

Thermal conductivity (ASTM C177) 

[(cal x cm)/(sec x  cm

2

 x ˚C)]  x 10

-3

1.37

1.39

2.65

1.23

1.73

1.58

Dielectric constant   

(ASTM D150 )    1 kHz

67.5

67.5

35.0

75.0

21.4

8.6

Dielectric strength  

(ASTM D149 )    volts/mil 

30

30

30

30

100

100

Maximum continuous dry 

service temperature   ˚F

250

250

200

250

250

250

Chemical Resistance

Devcon

® 

Plastic Steel

®

 

Putty 

(A)

Devcon

® 

Plastic Steel

® 

Liquid (B)

Devcon

® 

Plastic Steel

®

 

5 Minute

®

 Putty 

(SF)

Devcon

® 

Stainless Steel 

Putty 

(ST)

Devcon

® 

Aluminum 

Putty 

(F)

Devcon

® 

Aluminum 

Liquid (F-2)

ACIDS 
Acetic 10%
Hydrochloric 10%
Sulfuric 10%

ALCOHOLS 
Methanol
Isopropanol

 

KETONES 
Acetone
Methyl ethyl ketone

ALKALIS 
Ammonium hydroxide 20%
Sodium hydroxide 10%

HYDROCARBONS 
Gasoline (unleaded)
Mineral spirits

CHLORINATED  
HYDROCARBONS
1-1-1 Trichloroethane

SALTS 
Sodium chloride
Trisodium phosphate

Key:               Excellent               Very Good              Fair               Poor

18

Devcon

® 

 Bronze Putty

Bronze-filled epoxy putty for repairing 

bronze and brass bushings, shafts,  

castings and equipment parts. 

• Repairs and rebuilds areas where 

 

    brazing would be  undesirable or  

    impossible 

• Bonds securely to bronze alloys, brass,  

    copper, and ferrous metals  

Item # 

Size

10260 1lb

Devcon

® 

 FasMetal

™

High-performance, alumina-filled epoxy 

for making fast, dependable emergency 

repairs to leaks in pipes.

• Hardens in 5 minutes

• Economical and convenient 

 

Item # 

Size

10780 1lb

Devcon

® 

 Wear Resistant Putty 

(WR2)

Smooth, non-rusting, all-purpose epoxy 

putty for repairs requiring low-friction 

finishes, such as machine lathe beds.

• Bonds to steel, iron, aluminum, ceramic,  

    concrete, brass, and   some plastics 

• Contains wear-resistant fillers for low  

    friction applications  

Item # 

Size

11410 

1lb

11420 

3lb

Devcon

® 

 HVAC Repair (Special F)

Aluminum-filled epoxy adhesive for HVAC 

repairs.

• Repairs coils in compressors 

• Hardens to a rigid bond that can be  

    ground, drilled or tapped  

Item # 

Size

19770 1lb

Devcon

® 

 Underwater Repair (UW)

High-performance technology for repairing, 

patching, and rebuilding equipment in 

habitually wet environments, including 

under water. 

• Non-rusting; easy-to-mix and apply 

• Eliminates the need for substrate to be  

    thoroughly dry before repair  

Item # 

Size

10260 1lb

Metal-filled epoxy technology that allow for fast economical permanent repairs to power plant and mining equipment. 

They can be machined, tapped and drilled, and corrosion resistant to harsh chemicals.  These products are available in 

pourable versions that can be used to provide accurate detail reproductions for short run prototype mold patterns,  

holding fixtures and forming dies.

Devcon

® 

Cleaner Blend 300

Safe, multi-purpose, nontrichloroethane 

based degreaser for removing heavy 

grease and oil from metal surfaces. 

• Needs no rinsing; leaves no residue 

• Evaporates fast 

Item # 

Size

19510 1pt

Devcon

® 

Liquid Release Agent

Silicone release agent prevents Devcon’s 

epoxy and urethane compounds from 

sticking to patterns or mold surfaces.

• Produces a high gloss finish 

• Facilitates the accurate duplication 

    of intricate details

Item # 

Size

19600 1pt 

Metal Repair Epoxies

19

Key:               Excellent               Very Good              Fair               Poor

Physical Properties

Devcon

®  

Bronze Putty  

(BR)

Devcon

®  

Wear Resistant

Putty 

(WR-2)

Devcon

®  

Underwater

Repair Putty (UW)

Devcon

®  

FasMetal

™

Devcon

®  

HVAC Repair  

(Special F)

Color 

Bronze

Dark Grey

Grey

Grey

Grey

Mix ratio by weight / volume   

resin:hardener

9:1 / 3:1

9:1 / 4:1

1.4:1 / 1:1

 1.07:1 / 1:1

 0.9:1 / 1:1

Mixed viscosity   cP

Putty

Putty

Putty

Putty

40,000

Functional cure hours

16

16

24

1

16

Pot life minutes @ 75˚F

35

45

45

4

60

Specific volume inches

3

/pound

12.4

13.9

17.0

17.2

16.1

Coverage per pound  inches

2 

@ 1⁄4" 

thickness

50

56

68

69

64

Cured hardness  

(ASTM D2240)    Shore D 

85

85

82

90

85

Cured shrinkage  

(ASTM D2566)    inch/inch 

0.0010

0.0005

0.0020

0.0093

0.0008

Adhesive tensile shear  

(ASTM D1002)    psi 

2,680

2,200

2,685

2,000

2,500

Compressive strength  

(ASTM D695)    psi

8,540

9,800

5,625

12,700

8,420

Flexural strength  

(ASTM D790)    psi  

6,180

6,500

4,990

7,700

6,260

Modulus of elasticity  

(ASTM D638)    psi x 10

5

      

8.0

7.5

7.5

8.5

7.8

Coefficient of thermal expansion 

(ASTM D696) 

[(in)/(in x ˚F)] x 10

-6

33

32

18

32

29

Thermal conductivity (ASTM C177) 

[(cal x cm)/(sec x  cm

2

 x ˚C)]  x 10

-3

1.57

1.67

1.41

2.04

1.73

Dielectric constant   

(ASTM D150 )    1 kHz

75.0

6.3

8.6

18.6

21.4

Dielectric strength  

(ASTM D149 )    volts/mil 

25

400

150

370

100

Maximum continuous dry 

service temperature   ˚F

250

250

250

250

250

Chemical Resistance

Devcon

®  

Bronze Putty 

(BR)

Devcon

®  

Wear Resistant

Putty 

(WR-2)

Devcon

®  

Underwater

Repair Putty (UW)

Devcon

®  

FasMetal

™

Devcon

®  

HVAC Repair  

(Special F)

ACIDS 

Acetic 10%

Hydrochloric 10%

Sulfuric 10%

ALCOHOLS 

Methanol

Isopropanol

KETONES 

Acetone

Methyl ethyl ketone

ALKALIS 

Ammonium hydroxide 20%

Sodium hydroxide 10%

HYDROCARBONS 

Gasoline (unleaded)

Mineral spirits

CHLORINATED  

HYDROCARBONS

1-1-1 Trichloroethane

SALTS 

Sodium chloride

Trisodium phosphate

Technical Information

Korrobond crusher backing compounds are two component products used as shock absorbing compounds in 

cone crushing machines. Extensively used within the quarrying and mining industries, Korrobond has a  

worldwide reputation for reliability.  Korrobond products are formulated to produce a low viscosity, tough and 

flexible backing. Korrobond serves as a backing and reinforcing layer between machine parts and as a damper 

when subjected to impact and shock loads.

The Korrobond 95 product maintains cone-crushing machinery to an optimal level, ensuring peak performance and 

reliable solutions that;

• Prolong the life of the machinery while protecting against impact and shock vibrations

• Enhance productivity

• Offers maximum savings on labor

• Are easily applied by engineering personnel with minimal training

• Has a proven track record to perform in all types of cone crushers and climates

Crusher Backing Compounds

NOW AVAILABLE IN NORTH AMERICA

20

Technical Information

Korrobond 95

High-strength epoxy liquid for use in rod, ball, pebble 

and autogenous mills, as well as in cone and gyratory 

crushers.

• Easy to pour, low viscosity liquid

• Negligible shrink and low exothermic reaction,

    which assures consistent interface between    

    epoxy and manganese or steel surfaces 

Item # 

Size

81095        20lb kit

Chemical Resistance

Korrobond 95

ACIDS 
Acetic 10%
Hydrochloric 10%
Sulfuric 10%

ALCOHOLS 
Methanol
Isopropanol

KETONES 
Acetone
Methyl ethyl ketone

ALKALIS 
Ammonium hydroxide 20%
Sodium hydroxide 10%

HYDROCARBONS 
Gasoline (unleaded)
Mineral spirits

CHLORINATED HYDROCARBONS
1-1-1 Trichloroethane

SALTS 
Sodium chloride
Trisodium phosphate

Physical Properties

Korrobond 95

Color 

Red

Mix ratio by weight /  

volume resin:hardener

100:5.94 / 9.9:1

Mixed viscosity   cP

10,320

Functional cure hours

8-10

Pot life minutes @ 75˚F

56

Specific volume 

inches 

3

/pound

17.2

Coverage per kit 

inches 

2 

@ 1⁄4" thickness

349

1

Cured hardness  

(ASTM D2240)    Shore D 

85

Cured shrinkage  

(ASTM D2566)    inch/inch 

0.0006

Adhesive tensile shear  

(ASTM D1002)    psi 

5,300

Lap Sheer (psi)

1,179

Compressive strength  

(ASTM D695)    psi

13,510

Flexural strength  

(ASTM D790)    psi  

10,310

Coefficient of thermal 

expansion (ASTM D696) 

[(in)/(in x ˚F)] x 10

-6

22

Side Impact
(in - lbs)

41

Maximum continuous dry 

service temperature ˚F

250

 

1

  

Coverage in inches

2

 / 20.4 pound unit

21

Crusher Backing Compounds

Surface Preparation

General Surface Preparation
In general, the following steps will help 

you properly prepare a surface prior to 

applying Devcon

®

 products:

1)  Make sure the surface is completely 

dry. Moisture will adversely affect the 

strength of the bond to the surface.

2)  Remove all surface contamination 

(paint, rust and grime) by abrasive blast-

ing, sanding or other  

mechanical means.

3)  Degrease with Devcon

®

 Cleaner Blend 

300.

4)  Abrade the surface to roughen it and 

create a surface profile.

5) Use the appropriate Devcon

®

 primer.

For detailed surface preparation  

procedures, refer to the appropriate  

substrate category and tech data sheet.

Metal

To properly prepare a metal surface:

1)  If the surface is oily or greasy, degrease 

it with Devcon

®

 Cleaner Blend 300.

2)  Abrasive-blast the surface with 25-40 

grit (or coarser) to produce a good 

surface profile. If you cannot  

abrasive-blast the surface, use a 60 

grit or coarser sandpaper to achieve a 

similar result. 

3)  Immediately coat the metal surface with 

Flexane

®

 FL-10 Primer to prevent it from 

rusting.

4)  Make repairs as soon as possible after 

blasting the substrate to avoid oxidation 

or flash rusting.

Rubber

To properly prepare a rubber surface:

1)  Abrade the surface using a rubber rasp 

or a grinder with a wire wheel to produce 

a good surface profile. (Oils and con-

taminants imbedded in the rubber  

surface are typically released in this 

process.)

2)  Remove all oil and grease from the rub-

ber surface with Devcon

®

 Cleaner Blend 

300 and an abrasive pad.

3)  Wipe the surface with a clean, lint-free 

cloth continuously until black residue is 

no longer picked up by the white cloth.

4)  Prime the surface as follows:
   

  Rubber to metal:

 Coat all metal sur-

faces (including stainless steel and alu-

minum) with two coats of Flexane

®

 FL-10 

Primer. The primer will significantly 

improve adhesion of Devcon products 

to metal. 

Aluminum Surfaces

Oxidation on aluminum surfaces reduces 

epoxy adhesion. This oxidation film must 

be removed before repairing aluminum 

with Devcon

®

 Metal Repair Epoxies. 

To properly prepare an aluminum surface:

1)  Remove oxidation by mechanical means 

such as  

grit-blasting or by chemical means such 

as acid etching.

2)  Follow the General Surface Preparation 

guidelines.

The key to a successful repair is proper preparation and thorough cleaning prior to applying repair products or protective 

coatings.

22

     Rubber

   

  Rubber to metal (for immersion 

service):

  

Coat any metal that will be immersed 

in an aqueous solution with Flexane

®

 

FL-10 Primer and Flexane

®

 FL-20 

Primer. First apply the FL-10 Primer and 

let dry for 60 minutes. Next, coat with 

the FL-20 Primer. Let dry for 30 minutes 

before applying the Devcon

®

 product.

     

Rubber to rubber:

 Coat all gum rub-

bers, neoprene or cured urethanes with 

a thin coat of Flexane

®

 FL-20 Primer. 

For ultimate peel strength, use Surface 

Conditioner  (on rubber only).

    

 Rubber to concrete:

 Coat concrete 

with Flexane

®

 FL-20 Primer. Multiple 

coats may be necessary because  

concrete is very porous. Let the primer 

dry for 30 minutes between coats.

    

 Rubber to wood or fiberglass:

 Coat 

these surfaces with Flexane

®

 FL-20 

Primer. Soft woods will require a second 

coat due to their absorption  

characteristics. 

     When bonding rubber to other surfaces, 

contact Technical Service for a recom-

mendation on primers and surface  

preparation procedures.

If you have questions, please contact Technical Service: 1-855-489-7262

23

Concrete

To properly prepare a concrete surface:

1)  Degrease the surface with Devcon

®

 

Cleaner Blend 300 or any  

water-based emulsifying cleaner 

and rinse thoroughly. Multiple 

cleanings may be necessary. Power 

washers or steam cleaners are very 

effective and can reduce the number 

of passes needed to clean the surface. 

Let the surface dry thoroughly before 

proceeding.

2)  Remove any cap-curing agents that were 

applied to the concrete when it was 

poured. These agents form a dense, 

impenetrable finish, making it almost 

impossible for coatings to adhere to 

them. 

3)  Shot blast (Blastrac

®

) the concrete to 

create a porous surface profile. This 

will improve surface “wetting” and 

coating or repair product adhesion.

Wet Surfaces

In general, Devcon

®

 repair products and 

protective coatings will not adhere to wet 

surfaces. 

To properly repair a wet surface:

1)  Review the General Surface Preparation 

guidelines.

2)  Thoroughly dry the surface. (If you are 

using Devcon

®

 Underwater Repair Putty 

(UW), refer to Underwater Surfaces  

section.)

3)  Stop all leaks or seepage as follows:
    

 

t

 Shut off the flow or pressure;

    

t

  Fit a wooden peg or a sheet metal 

screw into the hole; or 

    

t

  Stuff wax, cork, plumber’s caulk, 

Mortite or a cloth into the opening. 

     If the leak is caused by corrosion, the 

sidewall might be weak. Open the orifice 

until sound metal is exposed and the wall 

is thick enough to be plugged.

4)  Remove surface condensation  

(sweating) or dampness with a heat gun 

or similar device.

Underwater Surfaces

To properly prepare an underwater surface:

1)  Remove all dirt, barnacles, flaking paint 

or algae/seaweed from the surface.

2)  Wipe the surface with a clean cloth to 

remove any film. Although you cannot 

degrease underwater, wiping and 

 turning a clean cloth will often remove 

any film from the surface.

3)  Abrade the surface if possible. (Use a 

file or other mechanical means.)

4)  Remove oxidation by mechanical means 

such as high-pressure water or grit-

blasting, or by chemical means such as 

acid etching.

Blastrac

®

 is a registered trademark of Blastrac, NA

Before

After

24

Agency Approvals

Specification

Product

Part #

Size

MIL-PRF-24176C, Type I

Plastic Steel

®

 Putty (A)

10110, 10120, 10130

1lb, 4lb, 25lb

MIL-PRF-24176C, Type I

Titanium Putty

10760, 10770

1lb, 2lb

MIL-PRF-24176C, Type I

Ceramic Repair Putty

11700

3lb

MIL-PRF-24176C, Type II

Aluminum Putty (F)

10610, 10620

1lb, 3lb

MMM-A-1754

Plastic Steel

®

 Liquid (B)

10210, 10220, 10230

1lb, 4lb, 25lb

MMM-A-1754

Aluminum Liquid (F-2)

10710, 10720

1lb, 3lb

ABS

Flexane

®

 Brushable

15350

1lb

ABS

Plastic Steel

®

 Putty (A)

10110, 10120, 10130

1lb, 4lb, 25lb

ABS

Plastic Steel

®

 5 Minute

®

 Putty (SF)

10240

1lb

ABS

Titanium Putty

10760, 10770

1lb, 2lb

ABS

Stainless Steel Putty (ST)

10270

1 lb

ABS

Bronze Putty

10260

1 lb

ABS

Ceramic Repair Putty

11700

3lb

ABS

Plastic Steel

®

 Liquid (B)

10210, 10220, 10230

1lb, 4lb, 25lb

ABS

Aluminum Liquid (F2)

10710, 10720

1lb, 3lb

ABS

Brushable Ceramic Red

11760, 11762

2lb, 12lb

ABS

Brushable Ceramic Blue

11765, 11767

2lb, 12lb

ABS

Brushable Ceramic White

11770

2lb

NSF/ANSI 61

Stainless Steel Putty

10270

1 lb

NSF/ANSI 61

Brushable Ceramic White

11770

2 lb

ANSI/NSF 61

NSF

®

Product Name   

 

 

 

 Item #   

 

 Size 

            Page

Devcon

®

 400ml Dispensing System   

 

 

15043, 15047 

 

Gun/Mix Nozzle 

 

Devcon

®

 Aluminum Liquid (F-2) 

 

 

 

10710, 10720 

 

1lb, 3lb 

16

Devcon

®

 Aluminum Putty (F) 

 

 

 

10610, 10620 

 

1lb, 3lb 

16

Devcon

®

 

Bronze 

Putty 

(BR)    10260 

  1lb 

18

Devcon

®

 Brushable Ceramic Blue 

 

 

 

11765, 11767 

 

2lb, 12lb 

14

Devcon

®

 Brushable Ceramic Red 

 

 

 

11760, 11762 

 

2lb, 12lb 

14

Devcon

®

 

Brushable 

Ceramic 

White 

   11770 

  2lb 

14

Devcon

®

 Carbide Putty   

 

 

 

10050, 10080 

 

3lb, 20lb    

               8 

Devcon

® 

Ceramic 

Repair 

Compound 

   11730 

  32lb 

14

Devcon

®

 

Ceramic 

Repair 

Putty 

   11700 

  3lb 

14

Devcon

®

 

Cleaner 

Blend 

300 

   19510 

  1pt 

18

Devcon

®

 Combo Wear (FC) 

 

 

 

11450 

 

 

9lb 

 

              8 

Devcon

®

 DFense Blok

™

 

    11330 

  30lb 

6

Devcon

®

 DFense Blok

™

 

Fast 

Cure 

(FC) 

   11350 

  9lb 

 

6

Devcon

®

 DFense Blok

™ 

Power Mixer

 

 

   11301 

  81lb 

6

Devcon

®

 DFense Blok

™

 

Quick 

Patch 

   11320 

  1lb 

6

Devcon

®

 DFense Blok

™

 Surface Wetting Agent (SWA) 

 

11340 

 

 

1 lb 

6

Devcon

®

 FasMetal

™

 

 

    10780 

  1lb 

18

Devcon

®

 Flex-Add

™

 

    15940 

  8oz 

 

12

Devcon

®

 Flexane

®

 80 Liquid 

 

 

 

15800, 15810 

 

1lb, 10lb 

12

Devcon

®

 Flexane

®

 80 Putty 

 

 

 

15280, 15850 

 

1lb, 4lb 

10

Devcon

®

 Flexane

®

 94 Liquid 

 

 

 

15250, 15260 

 

1lb, 10lb 

12

Devcon

®

 Flexane

®

 

Belt 

Repair 

Kit 

   15165 

  Kit 

10

Devcon

®

 Flexane

®

 

Brushable 

   15350 

  1lb 

10

Devcon

®

 Flexane

®

 Fast Cure Liquid   

 

 

15050 

 

 

400ml cartridge 

             10 

Devcon

®

 Flexane

®

 Fast Cure Putty 

 

 

 

15049 

 

 

400ml cartridge 

             10 

 

Devcon

®

 Flexane

®

 High Performance Putty 

 

 

15330 

 

 

1lb 

 10

Devcon

®

 Flexane

® 

Primer 

FL-10 

   15980 

  4oz 

12

Devcon

®

 Flexane

® 

Primer FL-20                                                                   

15985                                                 

4oz 

12

Devcon

®

 Flexane

® 

Primer FL-40                                                                   

15984                                                 

4oz 

12 

Devcon

®

 HVAC Repair (Special F) 

 

 

 

19770 

 

 

1lb 

 

            18   

Devcon

®

 

HV 

Tile 

Adhesive    11489 

  20lb 

8

Devcon

®

 

Liquid 

Release 

Agent 

   19600 

  1pt 

18

Devcon

®

 Plastic Steel

®

 5 Minute

®

 Putty (SF) 

 

 

10240 

  

 

1lb 

16

Devcon

®

 Plastic Steel

®

 Liquid B 

 

 

 

10210, 10220, 10230   

1lb, 4lb, 25lb   

             16 

Devcon

®

 Plastic Steel

®

 Putty A 

 

 

 

10110, 10120, 10130   

1lb, 4lb, 25lb                                    16 

Devcon

®

 

Stainless 

Steel 

Putty 

   10240 

  1lb 

16

Devcon

®

 

Tile 

Adhesive 

    11495 

  20lb 

 

8

Devcon

®

 

Titanium 

Putty 

    10760, 

10770 

 1lb, 

2lb 

14

Devcon

®

 Wear Guard

™

 

Fine 

Load 

   11470 

  30lb 

 

8

Devcon

®

 Wear Guard

™

 

High 

Impact 

   11460 

  30lb 

 

8

Devcon

®

 Wear Guard

™

 

High 

Load 

   11490 

  30lb 

 

8

Devcon

®

 Wear Guard

™

 

High 

Temp 

   11480 

  30lb 

 

8

Devcon

®

 Wear Guard

™

 

Ultra 

   11475 

  30lb 

 

8

Devcon

®

 Wear Resistant Putty (WR-2)  

 

 

11410, 11420 

 

1lb, 3lb 

18

Devcon

® 

Underwater 

Repair 

Putty 

(UW)   11800 

  1lb 

18

Korrobond 95 

 

 

 

 

81095 

 

 

20lb kit 

 

             21

10

Product Index

25

Devcon

®

 R-Flex

™

 

15550

4lb

10

MSDS/TDS

All MSDS and TDS are available on our website at www.devcon.com

Customer Service

All purchase orders are placed with ITW Polymers Adhesives North America.

Warranty

Warranty:  ITW Polymers Adhesives, North America will replace any material found defective.  Because of 

the storage, handling and application of this material is beyond our control, we can accept no liability for the 

reults obtained.

Disclaimer

All information is based on laboratory testing and is not intended for design purposes.  ITW Polymers 

Adhesives North America makes no representations or warranties of any kind concerning this data.

26

27

30 Endicott Street

Danvers, MA  01923

855-489-7262

www.itwwagroup.com

©2013 ITW Wear & Abrasion Group. All rights reserved. All trademarks are the property of Illinois Tool Works.